DESCRIPTION |
|
|
| |
|
|
| |
A
plastic cartridge containing a base resin consisting of polyester resins,
a catalyst consisting of an organic peroxide and inert fillers in a paste
form. |
|
| |
|
|
|
| |
|
|
WHERE
TO USE |
|
|
| |
|
|
| |
- As
a bonding agent
- Where
a waterproof bond is required.
- Where
a chemically resistant bond is required.
- Where
a vibration-proof bond is required.
- When
bonding near to an edge.
- Where
a stress free bond is required.
|
|
| |
PAM
Cartridge No. 1 will, when used correctly, provide a high strength bond,
which is waterproof, chemically resistant, vibration proof and stress
free. |
|
| |
It
has been specially formulated as a trixotropic, high strength grout for
the permanent anchoring of bolts into concrete or brickwork. It is equally
suitable for bonding together most materials found on construction sites,
(consult our Technical Dept. if in doubt). |
|
| |
|
|
|
| |
|
TYPICAL
PROPERTIES |
|
|
| |
Gel
and Cure Times: |
|
| |
TEMPERATURE |
5
degrees c |
10
degrees c |
20
degrees c |
30
degrees c |
|
GEL
TIME |
15
mins |
10
mins |
7
mins |
5
mins |
|
MINIMUM
CURE BEFORE LOADING |
3
hrs |
2
hrs |
1.5
hrs |
1
hr |
|
|
|
| |
|
| |
|
| |
Typical
tensile and shear strengths to B.S. 5080 in 25 Kn concrete: |
|
| |
FIXING
DIAMETER |
M8 |
M10 |
M12 |
M16 |
M20 |
|
TENSILE
(Kn) |
19.0 |
21.7 |
41.0 |
75.0 |
105.0 |
|
SHEAR
(Kn) |
13.5 |
16.5 |
29.5 |
49.0 |
72.0 |
|
|
|
| |
|
|
|
| |
|
PREPARATION |
|
|
| |
|
|
| |
Holes
should be formed a minimum of 2mm greater than the bolt to be inserted,
using rotary percussive drilling techniques. If it has been necessary
to diamond drill holes, then they should be roughened or under reamed. |
|
| |
Pre-cast
holes should have their sides roughened prior to filling. All dust, drilling
debris and other contaminants should be removed. Bars and bolts should
be de-greased and all rust removed. |
|
| |
|
|
|
| |
|
|
APPLICATION |
|
|
| |
|
|
| |
Remove
the cap and protective insert from the cartridge and screw on the static
mixer nozzle. Fit the cartridge into the applicator gun and gradually
apply pressure by activating the trigger until material exudes from the
end of the nozzle. Stop pressurising and allow the resin to flow until
a uniform colour is achieved. Insert the nozzle into the base of the hole
and activate the trigger, removing the nozzle slowly as the hole fills.
Once sufficient resin is in the hole, release the pressure, wipe excess
resin from the nozzle and place the stud to be fixed into the hole with
a twisting action to ensure all contact between hole side, resin and stud. |
|
| |
Allow
the resin to cure fully before loading. Partly used cartridges are re-usable.
Remove the mixing nozzle, wipe away surplus resin and replace the nose
plug and cap. |
|
| |
|
|
|
| |
|
|
STORAGE
LIFE |
|
|
| |
|
|
| |
At
least 12 months in manufacturers unopened cartridges in sealed containers
if stored between 4 and 20 degrees C. |
|
| |
|
|
| |
Approximate
number of fixings per cartridge: |
|
| |
BOLT
DIA. |
8mm |
10mm |
12mm |
16mm |
20mm |
24mm |
|
HOLE
DIA. |
10mm |
12mm |
14mm |
18mm |
22mm |
28mm |
|
HOLE
DEPTH |
80mm |
90mm |
110mm |
125mm |
170mm |
210mm |
|
|
|
|
|
| |
|
| |
|
| |
|
|
|
| |
|
|
APPLICATIONS |
|
|
| |
|
|
| |
Anchoring
of machinery. Permanent installation of reinforcement, dowelling and starter
bars, foundation bolts, hand rails, safety fences, wall ties, rail tracks,
tie-back anchors etc. |
|
| |
|
|
|
| |
|
|
ADVANTAGES |
|
|
| |
|
|
| |
- Excellent
adhesion.
- Rapid
strength gain.
- High
strength.
- Corrosion
resistant.
- Resistant
to
thermal recycling.
- Low
temperature cure.
- May
be used in overhead applications.
- Pre-packed
ready for use.
|
|
| |
|
|
|
| |
|
|